Problem with blasting is when you are talking about a paintball gun there are areas that can't be effectively blasted. If you miss a small section in a hole inside the body and then try to ano it you will have nothing more than a mess. Chrome and nickle will violently react with the sulfuric acid when power is applied. The part will turn black and the acid bath will turn white. Unfortunately I know this from experience.